Sintesis Komposit Zeolit Magnetit dengan Metode Ko-Presipitasi sebagai Adsorben Zat Warna Methylene Blue

---

ABSTRAK

Penelitian dilakukan dengan tujuan memperoleh komposit zeolit magnetit, menentukan
perbandingan karakter luas permukaan, morfologi, dan distribusi ukuran pori dari zeolit teraktivasi dan
zeolit magnetit, menentukan waktu kontak optimum dan pH optimum pada adsorpsi zat warna methylene
blue. Zeolit di aktivasi dengan asam HCl 1 M, sintesis magnetit zeolit dilakukan dengan mencampurkan
zeolit teraktivasi ke dalam larutan FeCl3.6H2O dan FeSO4.7H2O dan menambahkan larutan NH4OH sebagai
agen pengendap. Hasil sintesis zeolit magnetit dan zeolit teraktivasi digunakan sebagai adsorben zat warna
methylene blue. Analisis komposisi kristal dilakukan dengan X-Ray Diffraction (XRD), bentuk morfologi
dengan Scanning Electron Microscopy (SEM), luas permukaan dan distribusi ukuran pori dengan
Brunauer-Emmet-Teller (BET), uji kemampuan adsorpsi zat warna methylene blue dengan
Spektrofotometer Uv-Vis.
Hasil yang diperoleh dari penelitian ini adalah zeolit teraktivasi dan zeolit magnetit. Difraktogram
XRD menunjukkan adanya senyawa magnetit dari hasil sintesis ketika dibandingkan dengan standar. Hasil
SEM menunjukkan morfologi permukaan zeolit aktivasi berbentuk batang sedangakan zeolit magnetit
terlihat lebih homogen. Hasil dari BET menunjukkan luas permukaan zeolit teraktivasi lebih besar dari
zeolit magnetit, sedangkan distribusi ukuran pori zeolit magnetit lebih besar dari zeolit teraktivasi.
Kemampuan adsorpsi zat warna methylene blue oleh zeolit teraktivasi lebih baik dari zeolit magnetit,
keduanya memiliki kemampuan dalam mengadsorpsi zat warna methylene blue.
Kata kunci : Zeolit, Magnetit, Adsorpsi, Methylene blue

ABSTRACT

The research was carried out with the aim of obtaining zeolite magnetite composites, determining
the comparison of the surface area character, morphology, and pore size distribution of activated zeolite
and magnetite zeolite, determining optimum contact time and optimum pH in the adsorption of methylene
blue dyes. Zeolite was activated with 1 M HCl acid, synthesis of zeolite magnetite was carried out by mixing
activated zeolite into FeCl3.6H2O and FeSO4.7H2O solutions and adding NH4OH solution as settling agent.
The synthesis of zeolite magnetite and activated zeolite was used as an adsorbent for methylene blue dyes.
Analysis of crystal composition was carried out by X-Ray Diffraction (XRD), morphological forms with
Scanning Electron Microscopy (SEM), surface area and pore size distribution with Brunauer-Emmet-Teller
(BET), test of methylene blue dye adsorption ability with Uv-Vis Spectrophotometer.
The results obtained from this study are activated zeolite and magnetite zeolite. Diffractogram XRD
shows the presence of magnetite compounds from synthesis when compared to the standard. The SEM
results show the rod morphology of the activated zeolite surface while the zeolite magnetite looks more
homogeneous. The results of BET show that the surface area of activated zeolite is greater than magnetite
zeolite, whereas the zeolite magnetite pore size distribution is greater than activated zeolite. The adsorption
ability of methylene blue dyes by activated zeolite is better than magnetite zeolite, both of which have the
ability to adsorb methylene blue dyes.
Keywords : Zeolite, Magnetite, Adsorpstion, Methylene blue

---

Ketersediaan

1613C19III

1613 C 19-ii

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

KIMIA

No. Panggil

1613 C 19-ii

Penerbit

: ., 2019

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

530

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Eva Liyana

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar