Studi Sifat Optis Dan Uji Degradasi Rhodamin B Dengan Lapisan Tipis Seng Oksida Pada Penambahan Aluminium (Zno:Al) Konsentrasi Tinggi

---

ABSTRAK
Telah dilakukan sintesis dan deposisi lapisan tipis ZnO:Al di atas substrat kaca menggunakan metode sol-gel teknik spray coating. Penelitian ini bertujuan untuk melakukan studi degradasi zat warna rhodamin B menggunakan material fotokatalis ZnO:Al dengan variasi konsentrasi tinggi Al 0-20% yang didegradasi di bawah cahaya lampu UV-C, lampu halogen dan lampu pijar. Studi pengaruh pengadukan (stirrer) dipelajari untuk mengetahui proses homogenisasi pada proses degradasi. Karakterisasi sifat optis, morfologi dan komposisi bahan diuji menggunakan spektrofotometer UV-Vis dan SEM-EDX. Hasil karakterisasi sifat optis menunjukkan semakin meningkat konsentrasi Al pada ZnO akan menurunkan nilai celah pita energinya. Hasil fotodegradasi lapisan tipis ZnO:Al pada sampel rhodamin B 10 ppm di bawah sinar UV mempunyai kemampuan degradasi yang optimal pada ZnO:Al 5% dengan efisiensi degradasi sebesar 91,63%. Fotodegradasi lapisan tipis di bawah lampu halogen mempunyai kemampuan degradasi yang baik pada ZnO:Al 20% yaitu 66,83%. Sedangkan, fotodegradasi lapisan tipis di bawah lampu pijar tidak bekerja secara optimal sehingga hanya mampu mendegradasi rhodamin B sebesar 33,54%. Dari studi degradasi menunjukan bahwa semakin meningkatnya konsentrasi Al pada ZnO akan menyebabkan penurunan kemampuan degradasi di bawah sinar UV sedangkan pada sinar cahaya tampak, semakin meningkatnya konsentrasi tinggi Al akan optimal untuk fotodegradasi. Studi pengaruh stirrer terhadap fotodegradasi lebih baik daripada fotodegradasi tanpa proses stirrer.
Kata kunci : lapisan tipis, ZnO:Al, fotodegradasi dan rhodamin B

ABSTRACT

Synthesis and deposition of ZnO: Al thin film has been carried out above the glass substrate using sol-gel spray coating method. This study aims to degradation of rhodamin B using ZnO:Al photocatalyst material with variations in the high concentration of 0-20% Al which are photodegradated under UV light, halogen lamps and incandescent lamps. The study of the effect of stirrers was also studied to determine the process of homogeneation in photodegradation. Characterization of optical properties, morphology and composition of materials were tested using UV-Vis and SEM-EDX spectrophotometers. The results of the characterization of optical properties showed that the increasing concentration of Al at ZnO would reduce the value of the energy band gap. Photodegradation of thin film under UV light has optimal degradation ability in ZnO: Al 5% is able to degrade 10 ppm rhodamin B with efficiency by 91.63%. Photodegradation of the thin film under the halogen lamp has a good degradation ability in ZnO:Al 20%, which is 66.83%. Whereas, the photodegradation of thin film under incandescent lamps does not work optimally because it is only able to degrade rhodamin B by 33.54%. The degradation study shows that the increasing concentration of Al on ZnO will decrease its degradation ability under UV light. While for visible light, the higher the concentration of high Al will be optimal for photodegradation. The study of the effect of stirrer on photodegradation is better than photodegradation without a stirrer.
Keyword : thin film, ZnO:Al, photodegradation and rhodamin B

---

Ketersediaan

1375D19III

1375 D 19-ii

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

1375 D 19-ii

Penerbit

: ., 2019

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

515.243.2

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Muhammad Mirza

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar