Pengaruh Durasi Ultrasonikasi Metode Sol-Gel Terhadap Hidrofilitas Dan Sifat Anti Bakteri Lapisan Tipis Zno/Zno:Ag Double Layer Pada Proses Destilasi Air Laut

---

ABSTRAK
Telah dilakukan sintesis dan deposisi lapisan tipis double layer ZnO/ZnO:Ag di atas substrat kaca dengan variasi durasi ultrasonikasi menggunakan metode sol-gel dan teknik deposisi spray coating. Penelitian ini bertujuan untuk melakukan studi pengaruh durasi ultrasonikasi terhadap sifat optis, hidrofilitas, dan sifat anti bakteri dari lapisan tipis double layer ZnO/ZnO:Ag di bawah cahaya tampak pada proses fotodegradasi air hasil destilasi air laut. Karakterisasi sifat optis diuji menggunakan spektrofotometer UV-Vis, hidrofilitas diuji dengan pengamatan sudut kontak antara lapisan tipis dengan air, uji sifat anti bakteri diuji dengan perhitungan jumlah bakteri pada hasil fotodegradasi air hasil destilasi air laut. Hasil karakterisasi sifat optis menunjukkan bahwa bahwa semakin lama durasi ultrasonik menyebabkan absorbansi semakin tinggi, transmitansi semakin rendah, dan celah pita energi semakin rendah dengan hasil terbaik pada variasi durasi ultrasonikasi selama 30 menit dengan nilai celah pita energi sebesar 3,097 eV. Hasil uji hidrofilitas menunjukkan bahwa durasi ultrasonikasi menyebabkan lapisan tipis double layer ZnO/ZnO:Ag semakin bersifat hidrofilik. Sifat hidrofilitas terbaik ditunjukkan oleh variasi durasi ultrasonikasi 120 menit yang ditandai dengan perubahan sudut kontak lapisan tipis dengan air terbesar sebesar 45.01o. Hasil fotodegradasi pada air hasil destilasi air laut menunjukkan bahwa durasi ultrasonikasi dapat meningkatkan aktivitas fotokatalitik dari lapisan tipis double layer ZnO/ZnO:Ag dengan efisiensi degradasi terbaik sebesar 97,93% pada variasi durasi ultrasonikasi selama 30 menit.
Kata kunci : Fotodegradasi, hidrofilitas, lapisan tipis double layer ZnO/ZnO:Ag, Sifat Anti bakteri

ABSTRACT
Synthesis and deposition of double layer ZnO / ZnO: Ag has been carried out on a glass substrate with varying duration of ultrasonication using the sol-gel method and spray coating deposition technique. This study aims to study the effect of the duration of ultrasonication on optical properties, hydrophility, and anti-bacterial properties of a thin layer of double layer ZnO / ZnO: Ag under visible light in the process of photodegradation of water from seawater distillation. Characterization of optical properties was tested using a UV-Vis spectrophotometer, hydrophility was tested by observing the contact angle between the thin layer with water, the test of anti-bacterial properties was tested by calculating the number of bacteria on the results of photodegradation of water from sea water distillation. The results of characterization of optical properties showed that the longer the ultrasonic duration caused the absorbance to be higher, the transmittance was lower, and the energy band gap was lower with the best results on the variation of the duration of ultrasonication for 30 minutes with an energy band gap of 3,097 eV. The results of the hydrophility test show that the duration of ultrasonication causes a thin layer of double layer ZnO / ZnO: Ag to become more hydrophilic. The best hydrophility properties are indicated by variations in the duration of 120 minutes of ultrasonication which is characterized by a change in the contact angle of the thin layer with the largest water of 45.01o. Photodegradation results in seawater distilled water showed that the duration of ultrasonication could increase photocatalytic activity of a thin layer of double layer ZnO / ZnO: Ag with the best degradation efficiency of 97.93% in the variation of the duration of ultrasonication for 30 minutes.
Keyword: Anti-bacterial properties, double layer thin film ZnO/ZnO:Ag, hydrofility, photodegradation.

---

Ketersediaan

1369D19III

1369 D 19-ii

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

1369 D 19-ii

Penerbit

: ., 2019

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

515.2433

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

FISIKA ATOM DAN NUKLIR

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Ragil Adi Nugroho

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar