Penentuan Nilai Koefisien Serapan Bahan Kuningan dan Galvalum Terhadap Sinar-X Sebagai Alternatif Bahan Perisai Radiasi

---

ABSTRAK

Penelitian mengenai penentuan nilai koefisien serapan bahan kuningan dan galvalum untuk menganalisis kesetaraannya dengan timbal sebagai perisai radiasi. Perisai radiasi digunakan untuk melindungi pekerja radiasi maupun masyarakat umum. Dalam pengujian koefisien serapan bahan kuningan dan galvalum, pesawat diatur pada tegangan, arus dan waktu pada kondisi faktor eksposi 81 kV 32 mAs dan 90 kV 40 mAs yang tetap serta jarak antara fokus dengan objek sejauh 100 cm, luas lapangan penyinaran 5 cm x 5 cm. Pengukuran dilakukan dengan Multi Purpose Detector (MPD) yang diletakan di bawah objek, pusat sinar ditempatkan di tengah-tengah objek, kemudian dilakukan eksposi untuk masing-masing variasi ketebalan timbal, kuningan dan galvalum. Dari hasil pengujian koefisien serapan bahan pada kuningan dan galvalum pada faktor eksposi 81 kV 32 mAs diperoleh hasil nilai koefisien serapan untuk kuningan sebesar 3,378/mm dan galvalum sebesar 2,491/mm. Pada faktor eksposi 90 kV 40 mAs diperoleh hasil nilai koefisien serapan untuk kuningan sebesar 2,871/mm dan untuk galvalum sebesar 2,0657/mm. Hasil kesetaraannya antara kuningan dan galvalum dengan timbal pada faktor eksposi 81 kV 32 mAs untuk ketebalan 2 mm dibutuhkan 5,4 mm untuk kuningan dan 7,3 mm untuk galvalum.

Kata kunci: Pesawat sinar-X, Koefisien Serapan, Kuningan, Galvalum, Multi Purpose Detector (MPD)
 
ABSTRACT

Research on determining the absorption coefficient of brass and galvalume to analyze its equivalence with lead as a radiation shield. The radiation shield is used to protect radiation workers and the general public. In testing brass and galvalume material absorption coefficients, the plane is set to the voltage, current and time at 81 kV 32 mAs exposures and 90 kV 40 mAs fixed and the distance between focus and object is 100 cm, the irradiation field is 5 cm x 5 cm. Measurements were made with Multi Purpose Detector (MPD) placed under the object, the center of the beam was placed in the middle of the object, then the exposures were carried out for each variation of lead, brass and galvalume thickness. From the results of testing the absorption coefficient of material in brass and galvalume on the 81 kV 32 mAs exposure factor, the absorption coefficient value for brass is 3,378 / mm and galvalume is 2,491 / mm. In the exposures factor 90 kV 40 mAs, the absorption coefficient value for brass is 2,871 / mm and for galvalume is 2,0657 / mm. The equality results between brass and galvalume with lead in the 81 kV 32 mAs exposure factor for 2 mm thickness is required 5,4 mm for brass and 7,3 mm for galvalume.

Keywords: X-ray machine, Absorption Coefficient, Brass, Galvalume, Multi Purpose Detector (MPD)

---

Ketersediaan

1321D18IV

1321 D 18

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

1321 D 18

Penerbit

: ., 2018

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

004.6

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Aisyah Azizah Amirah

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar