Kajian Eksperimental Lucutan Plasma Korona Berarus Negatif Dengan Konfigurasi Elektrode Multi Titik-Bidang Terhadap Kain Polyester Weight Reduce

---

ABSTRAK

Penelitian tentang karakterisasi reaktor plasma berarus negatif konfigurasi elektrode multi titik-bidang dan penerapannya pada kain polyester weight reduce telah dilakukan. Penelitian ini memiliki beberapa tujuan yaitu mendapatkan karakteristik reaktor plasma berarus negatif baik tanpa sampel maupun dengan sampel kain polyester weight reduce, nilai mobilitas ion, karakteristik kain polyester weight reduce yang telah diiradiasi, hasil SEM (Scanning Electron Microscope), dan hasil mekanik. Penelitian ini digunakan reaktor plasma konfigurasi elektrode multi titik-bidang yang dihubungkan dengan pembangkit sumber tegangan tinggi DC. Variasi jarak antar elektrode sebesar 1,0 cm, 1,3 cm, 1,6 cm 1,9 cm, 2,2 cm, 2,5 cm, 2,8 cm dan 3,1 cm. Hasil penelitian menunjukkan bahwa semakin besar tegangan yang diberikan maka nilai arus yang dihasilkan semakin besar dan tegangan yang dibutuhkan untuk menghasilkan arus lebih tinggi dengan adanya bahan kain polyester weight reduce. Nilai tegangan dan arus tertinggi karakterisasi tanpa sampel terdapat pada jarak 3,1 cm dengan nilai arus 0,85 mA pada tegangan 27,86 kV, sedangkan dengan sampel memiliki nilai arus 0,40 mA pada tegangan 20,48 kV. Nilai mobilitas ion yang dihasilkan menunjukan bahwa semakin besar jarak elektroda yang diberikan maka semakin kecil mobilitas ionnya. Berdasarkan hasil uji tetes air menunjukan hasil bahwa semakin lama peradiasian kain, maka semakin cepat durasi serapnya. Hal ini ditunjukkan dengan jarak 2,5 cm pada durasi 5 menit didapatkan waktu penyerapan 2,79 sekon, sedangkan pada durasi 30 menit didapatkan 2,03 sekon. Pada uji SEM menunjukan hasil bahwa semakin lama waktu peradiasian, maka permukaan kain akan semakin rusak. Pada uji mekanik menunjukkan hasil bahwa semakin lama peradiasian pada kain, maka semakin kecil kekuatan kain polyester weight reduce. Hal ini ditunjukkan dengan variasi waktu 10 menit memiliki nilai kekuatan tahan jebol 994,4 kPa sedangkan pada variasi waktu 35 menit memiliki nilai kekuatan tahan jebol 953,4 kPa.

Kata kunci : Plasma korona, multi titik-bidang, mobilitas ion, kain polyester weight reduce, perlakuan tekstil 

ABSTRACT

Research on the characterisation of plasma reactor with negative current of multi square-point electrode configuration and its application on polyester weight reduce fabric has been done. This research has several objectives of obtaining characteristics of negative plasma reactor, either without sample or with the sample of polyester weight reduce fabric, ion mobility value, characteristics of irradiated polyester weight reduce fabric, SEM (Scanning Electron Microscope) results, and a mechanical result. The research is used a Plasma multi square-point electrode configuration Plasma reactor which is connected to a high-voltage DC power plant. Variations in distance between electrodes are 1.0 cm, 1.3 cm, 1.6 cm, 1.9 cm, 2.2 cm, 2.5 cm, 2.8 cm, and 3.1 cm. The results have shown that the greater voltage is given, the greater current value is resulted. And, the voltage which is needed to produce a higher current values is that the presence of a polyester weight reduce fabric. The highest voltage and current values of unsampled characterisation can be found at a distance of 3.1 cm with a current value of 0.85 mA at a voltage of 27.86 kV, compared to a sample with a current value of 0.4 mA at a voltage of 20.48 kV. The resulting ion mobility value indicates that the greater distance of the electrode is given, the smaller ion of the mobility. Based on the results of the water drop test showed that the longer the irradiation of the fabric, the faster duration of absorption. This is indicated by a distance of 2.5 cm in the duration of 5 minutes obtained the absorption time of 2.79 seconds, while in the duration of 30 minutes obtained 2.07 seconds. In the SEM test showed that the longer the irradiation, fabric surface will be more damaged. In the mechanical test shows that the longer the irradiation on the fabric, the smaller the strength of polyester weight reducing fabric. This is indicated by the time variation of 10 minutes has a breakthrough strength value of 994.4 kPa while at 35 minute time variation has a breakthrough strength value 953.4 kPa.

Keywords: Plasma corona, multi-point field, ion mobility, polyester weight reduce fabric, textile treatment.

---

Ketersediaan

1294D18III

1294 D 18

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

1294 D 18

Penerbit

: ., 2018

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

2365

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Yenni Eka Damayanti

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar