Pengaruh Laju Aliran Gas Osigen Dalam Sintesis Partikel Seng Oksida (ZnO) Menggunakan Metode Flame Spray Pyrolysis dan Aplikasi Untuk Mendegradasi Zar Warna Amaranth

---

INTISARI

Partikel seng oksida (ZnO) telah berhasil disintesis dari Zinc Nitrate Hexahydrate dengan molaritas 0.7 M dengan menggunakan metode Flame Spray Pyrolysis (FSP). Pada metode ini, oksigen digunakan sebagai gas pengoksida dan LPG dengan komposisi 97% campuran propana dan butana sebagai sumber bahan bakar. Pada penelitian ini, laju aliran gas oksigen divariasikan pada 1; 1,5; 2 dan 2,5 Liter Per Menit (LPM). Karakterisasi sifat optis, struktur kristal dan morfologi permukaan diuji menggunakan Spektrofotometer UV-Vis, XRD dan SEM. ZnO kemudian digunakan untuk fotodegradasi pewarna amaranth dengan konsentrasi 10 ppm menggunakan solar simulator selama 105 menit. Hasil karakterisasi XRD menunjukkan bahwa ZnO memiliki struktur kristal heksagonal. Citra SEM memperlihatkan partikel berbentuk bulat (spherical) dengan beberapa partikel berlubang (hollow).ZnO dengan laju aliran gas oksigen 1,5 LPM merupakan ZnO dengan aktivitas katalisis paling optimal. Uji usabilitas fotodegradasi dilakukan untuk mengetahui batas kemampuan partikel ZnO dalam melakukan fotodegradasi. Semakin banyak dilakukan pengukuran maka koefisien laju degradasi semakin menurun. Hasil pengukuran I hingga IV koefisien laju degradasi ZnO berturut-turut 0,00953; 0,00624; 0,00418 dan 0,00341.
Kata kunci : ZnO, Flame Spray Pyrolysis, LPG, oksigen , fotokatalis, fotodegradasi

ABSTRACT

ZnO particles were successfully synthesized from Zinc Nitrate Hexahydrate with molarity 0.7 M using Flame Spray Pyrolysys (FSP) method. In this method, oxygen were used as oxidizer and LPG with composition of 97% mixture of propane and butane, were used as fuel. The flow rates of oxygen during ZnO particle fabrication were 1, 1,5, 2, and 2,5 LPM. The characterizations ofoptical properties, cystalline structure and surface morphology determined by spectrophotometer UV-Vis, XRD, and SEM. ZnO then used to photodegradation of amaranth dye with concentration 10 ppm under irradiation of solar simulator for 105 minutes. XRD’s characterization showed ZnOhexagonal zincite crystalline structure formed. SEM image of ZnO showed spherical form which was the mixture of solid and hollow particles. . ZnO particles at 1,5 LPM flow rate was ZnO with the most optimal photocatalytic activity Resuability test of photodegradation was done to know the limits limit of ZnO particles in photodegradation. The more reusability test done, the coefficient of degradation rates decrease. The results of the 1st to the 4th coefficient of degradation rates of ZnO respectively 0.00953, 0.00624, 0.00418 and 0.00341.
Keywords : ZnO, Flame Spray Pyrolysis, LPG, oxygen, photocatalyst, photodegradation

---

Ketersediaan

1212D17IV

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

-

Penerbit

: ., 2017

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

1839

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Rizki Dwi Herdianti

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar