Studi Metode Laser Induced Shockwave Plasma Spectroscopy Untuk Identifikasi Keaslian Perhiasan Perak Menggunakan Laser Nd:YAG 1064 nm

---

INTISARI

Identifikasi keaslian perhiasan perak telah dilakukan dengan menggunakan metode Laser Induced Shockwaves Plasma Spectroscopy (LISPS). Plasma dibangkitkan dengan penembakan laser Nd:YAG (1064nm, 50mJ, 7 Hz) pada tekanan 1,5 torr ke permukaan target. Penelitian dilakukan untuk membedakan sampel perak 99,9%, perhiasan perak 92,5%, dan perhiasan imitasi dengan menghitung rasio intensitas Ag. Sampel perhiasan perak asli dan perhiasan imitasi masing-masing memiliki rasio intensitas sebesar 1,46, 1,29, 0. Spektrum emisi perak 99,9% menunjukkan kemiripan dengan perhiasan perak 92,5%. Namun perhiasan imitasi tidak menunjukkan kemiripan dan unsur Ag tidak terdeteksi. Batas deteksi unsur Ag adalah 2,74%, sementara terdeteksi unsur Fe dan Cu pada perhiasan perak 92,5% serta Fe, Cu, dan Zn pada perhiasan imitasi dengan panjang gelombang beragam. Sebagai pembanding, perhiasan imitasi juga dideteksi dengan menggunakan metode X-Ray Diffraction (XRD). Hasil dari metode XRD menjelaskan bahwa perhiasan imitasi memiliki struktur kristal Cu-Zn.

Kata Kunci: Laser Induced Shockwave Plasma Spectroscopy, analisa perhiasan, perak, rasio intensitas Ag

 
ABSTRACT

Identification of the authenticity of silver jewelry has been done using Laser Induced Shockwaves Plasma Spectroscopy (LISPS) method. Plasma is generated by laser firing Nd: YAG (1064nm, 50mJ, 7Hz) at a pressure of 1.5 torr to the target surface. The study was conducted to distinguish 99.9% silver samples, 92.5% silver jewelry, and imitation jewelry by calculating the intensity ratio of Ag. The original silver jewelry samples and imitation jewelry each had an intensity ratio of 1.46, 1.29, 0. The silver emission spectrum of 99.9% showed similarities with the 92.5% silver jewelry. However imitation jewelry does not show any resemblance and Ag element is not detected. The detection limit of Ag elements is 2.74%, while Fe and Cu are detected on 92.5% silver jewelry and Fe, Cu, and Zn on imitation jewelry of varying wavelengths. For comparison, imitation jewelry is also detected using X-Ray Diffraction (XRD) method. The results of the XRD method explain that the imitation jewelry has a Cu-Zn crystal structure.

Keywords: Laser Induced Shockwave Plasma Spectroscopy, Jewelry Analysis, Silver, Intensity ratio of Ag

---

Ketersediaan

1206D17IV

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

1206D17IV

Penerbit

: ., 2017

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

1833

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Ririn Widya Septianti

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar