Analisis Sifat Optis Lpaisan Tipis TiO2:N Untuk Fotodegradasi Pewarna Direct Blue 71

---

INTISARI

Lapisan tipis TiO2:N telah dideposisi di atas substrat kaca menggunakan metode
sol-gel spray coating. Aplikasi TiO2 telah banyak dilaporkan dalam berbagai bidang
salah satunya yaitu untuk fotodegradasi polutan organik. Celah energi TiO2 (~3,2
eV) membatasi aktivitas fotodegradasinya hanya pada rentang panjang gelombang
UV, sedangkan cahaya tampak dari matahari tersedia melimpah di bumi. Nitrogen
digunakan sebagai dopan agar dapat memperkecil celah energi TiO2, sehingga TiO2
dapat bekerja aktif pada rentang panjang gelombang cahaya tampak. Titanium (IV)
isopropoxide digunakan sebagai sumber Ti dan urea sebagai sumber nitrogen pada
larutan prekursor TiO2:N. TiO2:N dideposisikan di atas hotplate pada temperatur
450°C. Sifat optis, struktur kristal dan morfologi permukaan TiO2:N berturut-turut
diuji menggunakan spektrofotometer UV-Vis, XRD, dan SEM. Keberadaan
nitrogen dalam TiO2:N dianalisis menggunakan EDX. Kemampuan fotokatalitik
TiO2:N diuji untuk fotodegradasi pewarna DB 71 dengan konsentrasi 10 ppm di
bawah radiasi cahaya matahari dan lampu UV C selama 3 jam. Spektrum absorbansi
yang tinggi teramati pada rentang panjang gelombang 284 – 354 nm yang
menunjukkan TiO2:N menyerap cahaya didaerah UV. Celah energi TiO2:N yaitu
2,84 eV yang bersesuaian dengan celah energi TiO2 struktur rutile dan jenis doping
N interstisial. Hal itu diperkuat dengan pola XRD yang menunjukkan puncakpuncak dominan bidang TiO2 rutile (200), (210), (221), (321) dan satu puncak
brookite (032). Fotodegradasi DB 71 menggunakan TiO2:N lebih efektif
dibandingkan dengan TiO2 baik dengan sumber cahaya matahari maupun lampu
UV C.
Kata kunci : Lapisan tipis, TiO2:N, Fotodegradasi, Direct Blue 71

ABSTRACT

N-Doped TiO2 thin film has been deposided on glass substrate by sol gel spray
coating method. TiO2 applications has been reported in many field such as pollutant
organic photodegradation. The energy gap of TiO2 (~3,2 eV) made its
photodegradation activity limited only under UV wavelength, while visible light
from solar energy available all around the world. Nitrogen was used as dopant to
decrease the energy gap of TiO2 so it could work actively under visible light
wavelength. Titanium (IV) isopropoxide used as Ti source and urea as nitrogen
source in N-doped TiO2 precursor solution. N-doped TiO2 deposided on hotplate
with temperature 450°C. Optical properties, cystalline structure and surface
morphology of N-doped TiO2 were examinated in line by spectrophotometer UVVis, XRD, and SEM. Nitrogen existence in N-doped TiO2 was analysed by EDX.
Photocatalytic abililty of N-doped TiO2 was examinated for photodegradation dye
DB 71 with concentration of 10 ppm under solar energy irradiation and UV C light
for 3 hours. The highest absorbance spectrum was found in wavelength 284 to 354
nm showed that N-doped TiO2 absorbed light in UV wavelength. The energy gap of
N-doped TiO2 is 2,84 eV, refers to energy gap of TiO2 structure rutile and doping
N interstitial type. This result was reinforced by XRD pattern that showed dominant
peaks of TiO2 rutile plane of (200), (210), (221), (321) and one brookite’s peak
(032). Photodegradation of DB 71 is more effective using N-Doped TiO2 than TiO2
thin film under both solar light and UV C light irradiation.
Keywords : Thin film, N-Doped TiO2, Photodegradation, Direct Blue 71

---

Ketersediaan

1183D17IV

530,42 YUN a

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

530,42 YUN a

Penerbit

: ., 2017

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

1813

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Yunita Indriyani

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar