Sintesis Lapis Tipis Cu-ZnO/FTO Dengan Metode Elektrodeposisi Untuk Aplikasi Degradasi Methylene Blue

---

ABSTRAK

Sintesis lapis tipis telah dilakukan dengan membuat lapis tipis Cu-ZnO/FTO dengan prekursor Zinc Sulfate Heptahydrate dan Copper (II) Sulfate Pentahydrate. Lapis tipis Cu-ZnO/FTO dibuat dengan metode elektrodeposisi, kemudian digunakan untuk degradasi Methylene Blue dengan metode Fotokatalisis dan Fotoelektrokatalisis dan untuk keperluan karakterisasi XRD. Penelitian ini bertujuan untuk mensintesis lapis tipis Cu-ZnO/FTO dan mendegradasi Methylene Blue melalui proses fotokatalisis yang diujikan pada sinar UV-C dan tampak serta efek fotoelektrokatalisis pada degradasi Methylene Blue pada sinar tampak. Lapis tipis Cu-ZnO berhasil disintesis menggunakan metode elektrodeposisi 2 langkah pada potensial ZnO 2,6 V dan potensial Cu 1,9 V dengan luas 3,5 x 2 cm. Hasil analisis XRD menunjukkan bahwa Kristal ZnO terbentuk pada 2 theta 36,42o, 42,34o, 61,4o dengan ukuran kristal ZnO sebesar 31,65 nm dan bentuk wurtzite. Hasil penelitian menunjukkan bahwa keberadaan lapis tipis Cu-ZnO/FTO memberikan pengaruh terhadap degradasi Methylene Blue. Hal ini ditinjau dari hasil uji selama 8 jam menggunakan proses fotokatalisis sinar tampak dengan degradasi sebesar 24,11% lebih besar dari fotokatalisis sinar UV-C dengan degradasi sebesar 10,81%. Hasil degradasi mengalami kenaikan menggunakan sinar tampak dari proses fotokatalisis dengan degradasi sebesar 24,11% menjadi 30,85% pada proses fotoelektrokatalisis. Persentase degradasi diukur pada panjang gelombang maksimum 664 nm.

Kata kunci: Elektrodeposisi, Lapis Tipis, Fotokatalisis, Fotoelektrokatalisis

ABSTRACT

Thin layer synthesis has been done by making a thin layer of Cu-ZnO / FTO with Zinc Sulfate Heptahydrate and Copper (II) Sulfate Pentahydrate as precursor. The Cu-ZnO / FTO thin layer is prepared by electrodeposition method, then used for Methylene Blue degradation by Photocatalysis method and Photoelectrocatalysis and for XRD characterization purposes. This research aims to synthesize a Cu-ZnO / FTO thin layer and degrade Methylene Blue through a photocatalytic process tested on UV-C and visible light and photoelectrocatalytic effects of Methylene Blue degradation on visible light. The Cu-ZnO thin layer was successfully synthesized using a 2-step electrodeposition method at a ZnO potential of 2.6 V and a potential Cu of 1.9 V with an area of 3.5 x 2 cm. XRD analysis showed that ZnO crystals were formed on 2 theta 36,42o, 42,34o, 61,4o with ZnO crystal size 31,65 nm and wurtzite shape. The results showed that the presence of a thin layer of Cu-ZnO / FTO had an effect on the degradation of Methylene Blue. This is observed from the test results for 8 hours using the process of photocatalysis visible light with degradation of 24.11% larger than UV-C light photocatalysis with degradation of 10.81%. The degradation result increased by visible light from photocatalysis process with degradation of 24.11% to 30.85% in photoelectrocatalysis process. The percentage of degradation was measured at a maximum wavelength of 664 nm.

Keywords: Electrodeposition, Thin Layer, Photocatalysis, Photoelectrocatalysis

---

Ketersediaan

1397C17IV

541,37 FIK s

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

KIMIA

No. Panggil

541,37 FIK s

Penerbit

: ., 2017

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

1759

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

KOMPUTER-PROGRAM(ALGORITMA & PEMROGRAMAN)

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Fiky Agung Prakoso

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar