Pengaruh Waktu Ageing terhadap Produk Sintesis β-Trikalsium Fosfat (β-TCP, β-Ca3(PO4)2) dengan Metode Sol Gel Menggunakan Reaktan Ca(NO3)2.4H2O, P2O5, dan Pelarut C2H5OH

---

RINGKASAN

Beta-trikalsium fosfat (β–TCP) dapat dipakai sebagai pengganti tulang yang potensial karena bersifat biocompatible, bioresorbable, dan osteokonduktif. Beta-TCP dapat disintesis dengan mereaksikan senyawa kalsium dan fosfat dengan metode sol gel. Hasil sintesis dipengaruhi oleh beberapa faktor, yaitu sumber Ca dan P, rasio Ca/P, pelarut, waktu ageing, temperatur drying, waktu drying, temperatur firing, dan waktu firing. Tujuan penelitian ini adalah untuk mengetahui pengaruh variasi waktu ageing terhadap produk sintesis β–TCP dengan metode sol gel yang meliputi kemurnian produk, ukuran bulir kristal dan perubahan kristalinitas.
Pada penelitian ini sumber Ca dan P adalah Ca(NO3)2.4H2O dan P2O5, pelarut yang digunakan etanol (C2H5OH), temperatur drying 80oC selama 20 jam, temperatur firing 800oC selama 30 menit. Hasil sintesis dianalisis dengan FTIR dan XRD untuk mengetahui kemurnian produk, ukuran bulir kristal, dan perubahan kristalinitas.
Dari semua waktu ageing, produk sintesisnya sama yaitu β–TCP. Ukuran bulir kristal berfungsi terhadap waktu ageing. Ukuran bulir kristal terkecil diperoleh pada ageing 4 hari sebesar 45,040 nm dan terbesar pada ageing 5 hari sebesar 61,983 nm. Perubahan kristalinitas ditentukan dari nilai FWHM untuk puncak tertinggi pada variasi ageing. Nilai FWHM cenderung naik untuk waktu ageing 1-4 hari kemudian turun drastis pada ageing 5 hari.

SUMMARY

Beta-tricalcium phosphate (β-TCP) can be used as a potential bone replacement because it is biocompatible, bioresorbable, and osteoconductive. Beta-TCP can be synthesized by reacting calcium and phosphate compounds by sol gel method. The synthesis results are influenced by several factors, ie source Ca and P, Ca/P ratio, solvent, ageing time, drying temperature, drying time, firing temperature, and firing time. The purpose of this research is to know the effect of ageing time variation on β-TCP synthesis product with sol gel method which include purity of the product, size of the crystal grain and change crystallinity.
In this study the sources of Ca and P are Ca(NO3)2.4H2O and P2O5, the solvent used ethanol (C2H5OH), drying temperature 80oC during 20 hours, firing temperature 800oC during 30 minutes. The synthesis results were analyzed by FTIR and XRD to determine the purity of the product, the size of the crystal grain, and the change in crystallinity.
Of all ageing time, the synthesis product is the same ie β-TCP. The size of the crystal grain works against the ageing time. The smallest crystal grain size was obtained at ageing 4 days at 45.040 nm and the largest in ageing 5 days was 61,983 nm. The change in crystallinity is determined from the FWHM value for the highest peak in the ageing variation. FWHM values tend to go up for an ageing time of 1-4 days then drop drastically at 5-day ageing.

---

Ketersediaan

1386C17IV

541 RIN p

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

KIMIA

No. Panggil

541 RIN p

Penerbit

: ., 2017

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

1754

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Rini Suherniawati Yuningsih

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar