Deposisi, Karakterisasi Sifat Optik dan Uji Degradasi DB71 Pada Lapisan Tipis ZnO:Co Konsentrasi Tinggi

---

INTISARI

Telah berhasil dilakukan deposisi lapisan tipis ZnO:Co di atas substrat kaca
menggunakan metode spray coating dengan penambahan variasi doping Co sebesar
5%, 10%, 15%, 20% dan 25%. Lapisan tipis ZnO:Co selanjutnya digunakan untuk
mendegradasi larutan zat warna Direct Blue 71 dibawah iradiasi sinar matahari.
Larutan ZnO:Co disentesis dengan melarutkan Zinc acetate dehydrate
(ZnAc) ke dalam isopropanol lalu ditambahkan monoethanolamine (MEA) dan
cobalt nitrat pada temperatur ruang dengan konsentrasi dari ZnAc 0,3 M dan
perbandingan molar dari MEA dan ZnAc yaitu 1:1. Kemudian larutan diaduk
menggunakan magnetic stirrer pada temperatur 70oC selama 30 menit hingga
didapatkan gel yang jernih dan homogen. Gel ZnO:Co diletakkan pada spray hole
dan kemudian disemprotkan pada substrat kaca yang telah dipanasi pada temperatur
400oC.
Sifat optik lapisan tipis ZnO:Co dikarakterisasi menggunakan spektroskopi
UV-Vis. Hasil penelitian menunjukkan bahwa penambahan doping Co pada lapisan
tipis ZnO menghasilkan absorbansi yang cenderung meningkat pada sampel doping
Co pada konsentrasi 15%. Selain itu, semakin besar penambahan konsentrasi Co
akan memperkecil nilai celah pita energinya. Hasil pengujian fotodegradasi larutan
zat warna Direct Blue 71 pada fotokatalis ZnO:Co mampu mendegradasi zat warna
sebesar 16% pada semua sampel.
Kata kunci : Fotokatalis, Lapisan Tipis ZnO:Co, Spray Coating, Direct Blue 71

ABSTRACT

A thin layer of ZnO:Co was deposited on a glass substrate using a spray
coating method with the addition of Co doping variations of 5%, 10%, 15%, 20%
and 25%. The ZnO:Co thin film is further used to degrade the Direct Blue 71 dye
solution under sunlight irradiation.
ZnO:Co solution was synthesized by dissolving Zinc acetate dehydrate
(ZnAc) into isopropanol and then added monoethanolamine (MEA) and cobalt
nitrate at room temperature with concentration of ZnAc 0.3M and molar ratio of
MEA and ZnAc of 1:1. Then the stirred solution used a magnetic stirrer at a
temperature of 70oC for 30 minutes to obtain a clear and homogeneous gel. Gel
ZnO:Co is placed on a spray hole and then sprayed on a heated glass substrate at
400oC.
The optical properties of the ZnO:Co coating were characterized using UVVis spectroscopy. The results showed that the addition of Co doping on a thin layer
of ZnO resulted in an increasingly high absorbance in the Co doping sample at a
concentration of 15%. In addition, the greater concentration of Co will decrease
the value of the energy band gap. The results of photodegradation test of Direct
Blue 71 dye solution on ZnO:Co photocatalyst were able to degrade dye by 16% of
entire samples .
Keywords: Photocatalyst, Thin film ZnO:Co, Spray Coating, Direct Blue 71

---

Ketersediaan

1154D17III

530,42 AHM d

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

530,42 AHM d

Penerbit

: ., 2017

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

1713

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Ahmad Pradana

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar