Analisis Pengaruh Penambahan Binding Agent L- Metionin Pada PEDVB-NH2/Nanosilver Sebagai Material Antibakteri Pada Kain Katun

---

ABSTRAK
PEDVB-NH2/Nanosilver telah terbukti mampu menjadi material antibakteri pada kain
katun. Namun dalam pengaplikasiannya pada kain masih memiliki kelemahan dikarenakan daya
rekat material antibakteri ke kain yang rendah sehingga menurunkan efektifitas antibakteri
terutama setelah melalui proses pencucian kain. Oleh karena itu, dilakukan pengembangan
dengan penambahan binding agent L-metionin untuk meningkatkan kemampuan kain dalam
mengikat material antibakteri. Sehingga, tujuan dari penelitian ini yaitu untuk menganalisis
pengaruh penambahan binding agent L-metionin dalam sintesis PEDVB-NH2/AgNP sebagai
material antibakteri pada kain katun serta menganalisis karakteristik dan efektifitas material yang
dihasilkan. Sintesis komposit PEDVB-NH2/AgNP dilakukan secara ex situ dan dilapiskan pada
kain yang sebelumnya telah dilapisi dengan binding agent L-methionin melalui teknik spray
coating. Hasil yang diperoleh menunjukkan bahwa Penambahan binding agent L-metionin pada
kain terlapis PEDVB-NH2/AgNP dapat meningkatkan kemampuan antibakteri dengan kenaikan
persentase inhibisi 5,35 % terhadap bakteri S. aureus dan 4,54 % terhadap bakteri E.coli serta
memiliki ketahanan terhadap 10, 20, dan 30 kali pencucian dengan rata-rata penurunan
persentase inhibisi 3,05 % terhadap bakteri S. aureus dan 3,53 % terhadap bakteri E.coli yang
lebih rendah dibandingkan kain tanpa binding agent L-metionin dengan rata-rata penurunan
persentase sebesar 4,07 % terhadap bakteri S. aureus dan 6,06 % .Kain terlapis PEDVBNH2/AgNP dengan binding agent L-metionin memiliki morfologi permukaan kain dengan
distribusi yang lebih merata, absobtifitas air yang lebih rendah, dan sifat hidrofobisitas yang
lebih tinggi dibandingkan kain tanpa penambahan binding agent L-metionin.
Kata kunci : L-metionin, binding agent, PEDVB-NH2, AgNP, Antibakteri

ABSTRACT
PEDVB-NH2/Nanosilver has been proven to be an antibacterial material in cotton fabrics.
However, in its application to fabrics, it still has weaknesses due to the low adhesion of
antibacterial materials to fabrics, thereby reducing antibacterial effectiveness, especially after
going through the fabric washing process. Therefore, a development was carried out with the
addition of a binding agent L-methionine to increase the ability of the fabric to bind antibacterial
materials. Thus, the purpose of this study was to analyze the effect of adding binding agent Lmethionine in the synthesis of PEDVB-NH2/AgNP as an antibacterial material on cotton fabrics
and to analyze the characteristics and effectiveness of the resulting material. The PEDVBNH2/AgNP composite was synthesized ex situ and coated on a cloth previously coated with Lmethionine binding agent through a spray coating technique. The results obtained showed that
the addition of binding agent L-methionine to PEDVB-NH2/AgNP coated fabric could increase
the antibacterial ability by increasing the percentage of inhibition of 5.35% against S. aureus and
4.54% against E. coli bacteria and had resistance to 10, 20, and 30 washes with an average
decrease in the percentage of inhibition of 3.05% against S. aureus bacteria and 3.53% against
E. coli bacteria which is lower than the cloth without L-methionine binding agent with an
average decrease the percentage of 4.07% against the bacteria S. aureus and 6.06%.
Keywords: L-methionine, binding agent, PEDVB-NH2, AgNP, Antibacterial

---

Ketersediaan

1875C21IV

1875 C 21-iv

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

KIMIA

No. Panggil

1875 C 21-iv

Penerbit

: ., 2021

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

NONE

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Indah Salma Sausan

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar