Sintesis Nanopartikel Tembaga Oksida (CuO NPs) Menggunakan Metode Ablasi Laser Sebagai Antibakteri Streptococcus mutans

---

INTISARI

Nanopartikel Tembaga Oksida (CuO NPs) memiliki kemampuan sebagai agen antimikroba yang murah tetapi efektif. Nanopartikel CuO digunakan untuk menghambat pertumbuhan bakteri Streptococcus mutans yang menyebabkan karies gigi. Nanopartikel CuO disintesis dengan metode ablasi laser menggunakan laser Nd:YAG dan menghasilkan nanopartikel memiliki kemurnian yang tinggi, berukuran kecil, dan stabil. Nanopartikel CuO telah berhasil disintesis dengan medium berupa Polyvinylpyrrolidone (PVP) variasi konsentrasi 0,5 mM, 5 mM, dan 10 mM. Hasil sintesis memperoleh nanopartikel CuO yang terbaik pada medium PVP berkonsentrasi 10 mM. Parameter yang dinilai dari penelitian ini meliputi ukuran, morfologi, kestabilan, dan kandungan nanopartikel CuO, serta aktivitas antibakteri nanopartikel CuO terhadap bakteri Streptococcus mutans. Hasil karakterisasi Particle Size Analyzer (PSA) menunjukkan nanopartikel CuO telah terbentuk nanopartikel dengan ukuran yang terkecil 3,615 nm pada medium 10 mM dan stabil setelah pengujian perbandingan puncak penyerapan spektrum UV-Vis pada usia sampel hari pertama dengan hari ketigapuluh. Karakterisasi Fourier Transmform Infra Red (FTIR) menunjukkan koloid nanopartikel tembaga memiliki kemurnian yang tinggi dibuktikan dengan keberadaan gugus CuO pada koloid. Uji aktivitas bakteri menggunakan metode difusi cakram menunjukkan nanopartikel berhasil membunuh bakteri dari hasil pembentukan zona hambat pada nanopartikel CuO dengan kadar yang berbeda. Zona hambat terbaik 2,75 mM pada pemberian nanopartikel CuO sebanyak 40 ppm..
Kata kunci : nanopartikel tembaga oksida, ablasi laser, karies gigi, bakteri Streptococcus mutans, agen antibakteri



ABSTRACT

Copper Oxide Nanoparticles (CuO NPs) have the ability as an inexpensive but effective antimicrobial agent. CuO nanoparticles are used to inhibit the growth of Streptococcus mutans bacteria which cause dental caries. CuO nanoparticles were synthesized by laser ablation using the Nd: YAG laser and producing nanoparticles having high purity, small, stable, and stable. CuO nanoparticles were successfully synthesized with a medium in the form of Polyvinylpyrrolidone (PVP) concentration variation of 0.5 mM, 5 mM, and 10 mM. The best synthesis of CuO nanoparticles was received on PVP medium collected 10 mM. The parameters released from this study include the size, morphology, stability, and content of CuO nanoparticles, as well as the antibacterial activity of CuO nanoparticles against Streptococcus mutans. The results of the Particle Size Analyzer (PSA) characterization showed that CuO nanoparticles had formed nanoparticles with sizes reaching 3,615 nm on a 10 mM medium and were stable after being examined according to determining the direction of the UV-Vis combination on the first day with the thirtieth day. Characterization of Fourier Transmform Infra Red (FTIR) shows colloidal copper nanoparticles having higher purity as evidenced by the content of CuO groups in colloids. Bacterial activity test using the disk diffusion method showed that nanoparticles succeeded in removing bacteria from the results of inhibition zone formation in CuO nanoparticles with different levels. The best inhibition zone is 2.75 mM when giving CuO nanoparticles of 40 ppm.

Keywords: copper oxide nanoparticles, laser ablation, dental caries, Streptococcus mutans bacteria, antibacterial agents

---

Ketersediaan

1475D20IV

1475 D 20-iv

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

1475 D 20-iv

Penerbit

: ., 2020

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

NONE

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Inayah Mumpuni Budiati

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar