Sintesis dan Karakter Sifat Optik Carbon Nanodots dari Asam Sitrat dan Urea Serta Uji Sensitivitasnya Terhadap Ag+

---

ABSTRAK
Sintesis material C-Dots dari asam sitrat menggunakan metode microwave
irradiation pada kondisi 450 W selama 30 menit dengan variasi penambahan urea
telah berhasil dilakukan. Tujuan dari penelitian ini adalah mengetahui karakteristik
dari material C-Dots serta menguji sensitivitasnya terhadap Ag+. Karakteristik optik
material C-Dots dilakukan melalui uji UV-Vis, uji fluoresensi dan analisis FTIR.
Hasil karakterisasi UV-Vis menunjukkan munculnya dua puncak yaitu pada
panjang gelombang 333 nm dan 410 nm. Pengukuran UV-Vis menunjukkan bahwa
material C-Dots optimal pada spektrum ultraviolet. C-Dots mempunyai energi gap
pada rentang 2,5-2,69 eV. Hasil dari uji fluoresensi menunjukkan emisi tertinggi
pada panjang gelombang 545 nm untuk material C-Dots dengan variasi urea 4 gram.
Analisis FTIR mengindikasikan adanya serapan khas dari C-Dots, yaitu gugus OH pada 3250 cm-1, N-H pada 3376 cm-1, C-H pada 750 cm-1 gugus C=O pada
bilangan gelombang 1640 cm-1. Uji sensitivitas material C-Dots terhadap logam
berat menggunakan Ag+. Perak Nitrat (AgNO3) sebagai penghasil ion Ag+. Hasil
uji sensitivitas C-Dots terhadap Ag+ dapat dilihat dari pendaran C-Dots
menggunakan lampu UV-C. Pada uji FTIR didapatkan adanya gugus AgNO3.
Kata Kunci: Ag+, C-Dots, Fluoresensi, Lampu UV-C, Microwave

ABSTRACT
Synthesis of C-Dots material from citric acid using the microwave irradiation
method at 450 W for 30 minutes with variations in the addition of urea has been
successfully carried out. The purpose of this study is to determine the
characteristics of C-Dots material and test its sensitivity to Ag+. The optical
characteristics of C-Dots material were carried out through UV-Vis test,
fluorecence test and FTIR analysis. UV-Vis characterization results showed the
emergence of two peaks, namely at 333 nm and 410 nm wavelengths. UV-Vis
measurements show that the C-Dots material is optimal in the ultraviolet spectrum.
C-Dots have energy gaps in the range of 2.5-2.69 eV. The results of the fluorecence
test showed the highest emission at a wavelength of 545 nm for C-Dots material
with 4 gram urea variation. FTIR analysis indicated a typical absorption of C-Dots,
namely the O-H group at 3250 cm-1, N-H at 3376 cm-1, C-H at 750 cm-1 the C = O
group at wave number 1640 cm-1. Test the sensitivity of C-Dots material to heavy
metals using Ag+. Silver Nitrate (AgNO3) as Ag+ ion producer. The results of the
sensitivity test of C-Dots against Ag+ can be seen from the luminescence of C-Dots
using UV-C lamps. The FTIR test the AgNO3 group was found.
Keywords: Ag+, C-Dots, Fluorecence, Microwave, UV-C lamp

---

Ketersediaan

1431D20I

1431 D 20-i

Perpustakaan FSM Undip (Referensi)

Tersedia

Informasi Detail

Judul Seri

FISIKA

No. Panggil

1431 D 20-i

Penerbit

: ., 2020

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

621.3916

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Novita Indah Pratiwi

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar